MIL-PRF-13830B
3.7 Optical component details.
3.7.1 Temperature operation. Cemented components as a result of exposure to
ambient air temperatures of minus 80 ± 2 degrees and plus 160 ± 2 degrees F shall
not develop "feathering", show evidence of separation or softening of cement or other
defect, except as specified in 3.6, with the provision that the increase or development
of edge separation or edge cement defects shall be cause for rejection.
3.7.2 Relative humidity - temperature operation. Cemented components as a
result of exposure to an ambient atmosphere of plus 130 ± 2 degrees F temperature,
and at least 95 percent minimum relative humidity, and subsequent exposure to
ambient air temperature of minus 80 ± 2 degrees and plus 160 ± 2 degrees F, shall
not develop "feathering", show evidence of separation or softening of cement or other
defects, except as specified in 3.6.
3.7.3 Reflection reducing films. Optical surfaces specified on drawings as
"surfaces to be coated" shall be coated with a reflection reducing film (see 3.2.5).
3.7.4 Optical blackening. When specified, ground surfaces of optical elements
shall be blackened with a finish approved by the responsible technical activity.
3.7.5 Resolution. Resolution tests shall be performed on each objective, collective,
erector, eyepiece, mirror, wedge, window, filter, prism and prism assembly (optical) as
specified in 4.2.5.
3.7.6 Parallelism, filters. Parallelism of filters shall be within the tolerance
specified on the drawings. When no tolerance is specified, filters located internally or
in front of a telescope shall not exceed 1 minute of arc light deviation. Filters located
between the eyelens and the exit pupil shall not have a light deviation exceeding 5
minutes of arc.
3.7.7 Reticle scale spacing. Reticle scale spacing shall be tested in accordance
with 4.2.10.5.
3.7.8 Polished surfaces. Polished surfaces shall show no evidence of grayness or
stain when inspected in accordance with 4.2.2.
3.7.9 Lenses.
3.7.9.1 Surface quality. Surface quality of each lens shall be in accordance with
applicable drawings or instrument specifications. When not specified, the surface
quality shall be as follows: Objectives, erectors, windows and other elements which lie
at least fifteen diopters out of the focal plane, shall have a surface quality of 80-50 or