MIL-PRF-13830B
3.7.10.2 Fractures and edge chips. Edge chips which do not encroach on the free
aperture of the prism shall be allowable within the following limitations: The sum of
the chip widths shall not exceed 30 percent of the length of edge on which the chips
occur. Chips shall be measured from the bevelling edge, not from sharp edge; i.e. after
bevelling and not before. Chips less than 1/2mm shall not be counted and not stoned;
chips larger than 1/2mm shall be stoned. Encroachment of chips shall be measured
on the faces of the prism from the bevelled edges. If the nominal length (measured to
sharp corner before bevelling) of the shortest edge of the prism which is adjacent to
any polished face is an inch or less, chips may encroach the faces 1mm; if said length
exceeds 25.4mm chips may encroach 2mm. This shall be permissible provided that
there are no edge chips which interfere with mounting or sealing and the chips do not
encroach upon the free aperture. Fractures visible to the unaided eye on any surface
or edge are not permitted.
3.7.10.3 Drawing requirements. The deviation of angle errors, pyramidal error or
error due to pyramid, spherical power, astigmatism, resolution, and image tilt shall be
as specified on the drawings.
3.7.10.4 Erecting prisms. Erecting prisms shall be inspected as specified in
4.2.5.2.
3.7.10.5 Reflecting surfaces - silvered or aluminized.
3.7.10.5.1 Edges. The edges of partially silvered surfaces of ocular prisms shall be
sharp and shall be free of irregularities when inspected with the aid of a magnifier of at
least the power of the eyepiece of the instrument to which the prism pertains.
3.7.10.5.2 Defects. Defects on reflecting surfaces appear the same as defects on
other optical surfaces and shall be treated in the same manner as specified in 3.7.10.1.
3.7.10.5.3 Aperture surfaces. Aperture surfaces of prisms through which light is
to be transmitted shall be free from particles of silver or aluminum remaining from
processing of other surfaces.
3.7.11 Reticles.
3.7.11.1 Surface quality. The surface quality shall be as specified on the drawings.
When not so specified the surface quality shall be as specified for focal planes in
3.5.5.3, except for zone sizes. The central zone shall be the central area, one half the
free aperture in width, for reticles having reticle graduation extremities within this
area, and those reticles having horizontal and vertical lines without graduations
outside the area. Reticles having graduations outside the central area, one half the
free aperture in width, the central zone shall be the central area, three-fourths the free